Baritle Emprenyenin (BaSO4) Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkisi

TAN, Hüseyin; ULUSOY, Hatice; PEKER, Hüseyin

Baritle Emprenyenin (BaSO4) Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkisi

Hüseyin TAN, (Department of Materials and Materials Processing Technology, Vocational School of Technical Sciences, Recep Tayyip Erdoğan Üniversity, 53100 Rize, Turkey.)

Hatice ULUSOY, (Department of Forest and Forest Prodution, Köyceğiz Vocational School, University Of Muğla Sıtkı Koçman, 48800, Muğla, Turkey.)

Hüseyin PEKER (Department of Forest Industrial Engineering, Forest Faculty, Artvin Çoruh University, 08000 Artvin, Turkey.)

Bartın Orman Fakültesi Dergisi

3 2

Yıl: 2017 Cilt: 19 Sayı: 2 Sayfa Aralığı: 160 - 165 Metin Dili: Türkçe İndeks Tarihi: 29-07-2022

Baritle Emprenyenin (BaSO4) Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkisi

Öz:

Bu çalışmada, baritin ahşapta emprenye etme özellikleri ilk kez araştırılmıştır. Çevreyle ilgili insan sağlığına zararsız olduğu için, bu doğal materyali çeşitli alanlarda (ör. Mobilya ve inşaat) kullanımı amaçlanmıştır. Barit (BaSO4) solüsyonu farklı konsantrasyonlarda barit (% 1, % 3, % 5) ile hazırlanmış ve ASTM-D 1413-76 standartlarına göre emprenye işlemi yapılmıştır. Bu çalışmada, ağaç türleri olarak Doğu Karadeniz bölgesinden alınan Sarıçam (Pinus sylvestris L.) ve Doğu Kayını (Fagus orientalis Lipsky) kullanılmıştır. Sonuçlar; her iki ahşap türünde, emprenye solüsyonundaki barit konsantrasyonunun artmasıyla, retensiyon %, fiziksel özellikler ve mekanik özelliklerin arttığını göstermiştir. En yüksek yoğunluk (0.63 g/cm3), elastikiyet modülü (16920 N/mm²), eğilme direnci (160.40 N/mm²) ve dinamik eğilme direnci (2.78 kpm/cm2) değerleri, sırasıyla, %1, %5, %50 ve %50'lik derişime sahip çözeltilerle emprenye edilen Kayın odunu örneklerinde elde edilmiştir.

Anahtar Kelime:

Konular: Biyoloji Malzeme Bilimleri, Özellik ve Test Malzeme Bilimleri, Kâğıt ve Ahşap İmalat Mühendisliği Orman Mühendisliği Malzeme Bilimleri, Kompozitler

The Effects of Impregnation with Barite (BaSO4) on the Physical and Mechanical Properties of Wood Materials

Öz:

The aim of the study was to investigate the effects of Barite on the physical and mechanical properties of wood. Barite as an impregnation material was used to be harmless to environment-related human health. Barite (BaSO4) solution was prepared with different concentrations of barite (1%, 3%, 5%), and the impregnation process of the samples were conducted according to ASTM-D 1413-76. Scotch pine (Pinus sylvestris L.) and Oriental Beech (Fagus orientalis L.) obtained from the Eastern Black sea region in Turkey were used. According to the results, it showed that each wood types, retention ratio, physical properties, and mechanical properties increased with increasing concentration of barite in the impregnation solution. For the Beech wood, the highest air-dried and dried densities were found to the samples impregnated with solution that had a 1% concentration (0.63 g/cm3); the highest modulus elasticity (MOE) was in samples impregnated with solution that had a 5% concentration (16920 N/mm²); the highest bending strength (MOR) was in samples impregnated with solution that had a 50% concentration (160.40 N/mm²); and the highest dynamic bending strength was in the beech impregnated with solution that had a 50% concentration (2.78 kpm/cm2).

Anahtar Kelime:

Konular: Biyoloji Malzeme Bilimleri, Özellik ve Test Malzeme Bilimleri, Kâğıt ve Ahşap İmalat Mühendisliği Orman Mühendisliği Malzeme Bilimleri, Kompozitler

Belge Türü: Makale Makale Türü: Araştırma Makalesi Erişim Türü: Erişime Açık

1. Arsenault, R. D. (1973). "Factors influencing the effectiveness of preservative systems," in: Wood Deterioration and its Preservation by Preservative Treatments, Vol.II, Preservatives and Preservatives Systems, (Editor: Darrel D. Nıcholas), Syracuse University Press, Syracuse, NY, pp. 121-278.
2. ASTM D 1413-76, (1976). "Standard methods of testing wood preservatives by laboratory soilblock cultures," ASTM International, West Conshohocken, PA.
3. Atar, M., and Keskin, H. (2007). "Impacts of coating with various varnishes after impregnation with boron compounds on the combustion properties of Uludağ fir," Journal of Applied Polymer Science 106(6), 4018- 4023. DOI: 10.1002/app.27072
4. Bal, B. C. (2006). Investigation of Some Physical and Mechanical Properties of Scots Pine (Pinus sylvestris L.) Wood Treated with Ammonical Copper Quat (ACQ), M.S. thesis, Institute of Science, Kahramanmaraş Sütçü İmam University, Kahramanmaraş, Turkey.
5. Baysal, E. (2011). "Combustion properties of calabrian pine impregnated with aqueous solutions of commercial fertilizers," African Journal of Biotechnology 10(82), 19255-19260. DOI: 10.5897/AJB11.3054
6. Kartal, S. N. (1998). Characteristics of Strength, Leaching and Durability of Wood Material Protected by CCA Wood Preservatives, Ph.D. thesis, Institute of Science, İstanbul University, İstanbul, Turkey.
7. Koski, A. (2008). Applicability of Crude Tall Oil for Wood Protection, Ph.D thesis, Department of Process and Environmental Engineering, Faculty of Technology, University of Oulu, Finland.
8. Lekili, M. (2002). "Padding-quality barite," Mining Newsletter 63, 28-30.
9. Le Van, S. L., and Winandy, J. E. (1990). "Effects of fire retardant treatments on wood
10.strength: A review," Journal of Wood and Fiber Science 22(1), 113-131.
11.Örs, Y., Atar, M., and Peker, H. (1999). "Effects of some wood preservatives on the density of Scotch pine and beech wood," Journal of Turkish Agriculture and Forestry 23(5), 1169-1179.
12. Peker, H., Sivrikaya, H., Baysal, E., and Yalınkılıç, M. K. (1999). "Static bending strength of wood treated with fire retardant and water repellent preservation chemicals," Pamukkale Journal of Engineering and Science 5(1), 975-983.
13.Richardson, B. A. (1978). Wood Preservation, Construction Press, Lancaster, UK.
14. Şen, S. (2007). "Pressure Impregnation System in Preservation of Wood Material"(http://www.emprenyebasinclikaplar.com/basincli-emprenye-sistemleri.html).Toker, H. (2007). Determination of Effects of Boron Compounds on Some Physical, Mechanical and Biological Properties of Wood, Ph.D. thesis, Institute of Science, Gazi Üniversity, Ankara, Turkey.
15.TS 2470 (1976). "Wood-Sampling methods and general requirements for physical and mechanical tests," Turkish Standards Institute, Ankara, Turkey.
16.TS 2472 (1976). "Wood-Determination of density for physical and mechanical tests," Turkish Standards Institute, Ankara, Turkey.
17.TS 2474 (1976). "Wood-Determination of ultimate strength in static bending," Turkish Standards Institute, Ankara, Turkey.
18.TS 2477 (1976). "Wood-Determination of impact bending strength," Turkish Standards Institute, Ankara, Turkey.
19.Yalınkılıç, M. K. (1993). Changes Caused by Various Wood Preservatives on the Properties of Combustion, Hygroscopicity, and Dimensional Stability and Washability of This Materials from Wood, Associate Professor thesis, Forest Faculty, Karadeniz Technical Üniversity, Trabzon, Turkey.
20.Yıldız, Ü. C., Temiz, A., Gezer E. D., and Yıldız, S. (2004). "Effects of the wood preservatives on mechanical properties of yellow pine (Pinus Sylvestris L.) wood," Building and Environment 39(9), 1071-1075. DOI: 10.1016/j.buildenv.2004.01.032

APA	TAN H, ULUSOY H, PEKER H (2017). Baritle Emprenyenin (BaSO4) Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkisi. , 160 - 165.
Chicago	TAN Hüseyin,ULUSOY Hatice,PEKER Hüseyin Baritle Emprenyenin (BaSO4) Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkisi. (2017): 160 - 165.
MLA	TAN Hüseyin,ULUSOY Hatice,PEKER Hüseyin Baritle Emprenyenin (BaSO4) Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkisi. , 2017, ss.160 - 165.
AMA	TAN H,ULUSOY H,PEKER H Baritle Emprenyenin (BaSO4) Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkisi. . 2017; 160 - 165.
Vancouver	TAN H,ULUSOY H,PEKER H Baritle Emprenyenin (BaSO4) Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkisi. . 2017; 160 - 165.
IEEE	TAN H,ULUSOY H,PEKER H "Baritle Emprenyenin (BaSO4) Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkisi." , ss.160 - 165, 2017.
ISNAD	TAN, Hüseyin vd. "Baritle Emprenyenin (BaSO4) Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkisi". (2017), 160-165.

APA	TAN H, ULUSOY H, PEKER H (2017). Baritle Emprenyenin (BaSO4) Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkisi. Bartın Orman Fakültesi Dergisi, 19(2), 160 - 165.
Chicago	TAN Hüseyin,ULUSOY Hatice,PEKER Hüseyin Baritle Emprenyenin (BaSO4) Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkisi. Bartın Orman Fakültesi Dergisi 19, no.2 (2017): 160 - 165.
MLA	TAN Hüseyin,ULUSOY Hatice,PEKER Hüseyin Baritle Emprenyenin (BaSO4) Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkisi. Bartın Orman Fakültesi Dergisi, vol.19, no.2, 2017, ss.160 - 165.
AMA	TAN H,ULUSOY H,PEKER H Baritle Emprenyenin (BaSO4) Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkisi. Bartın Orman Fakültesi Dergisi. 2017; 19(2): 160 - 165.
Vancouver	TAN H,ULUSOY H,PEKER H Baritle Emprenyenin (BaSO4) Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkisi. Bartın Orman Fakültesi Dergisi. 2017; 19(2): 160 - 165.
IEEE	TAN H,ULUSOY H,PEKER H "Baritle Emprenyenin (BaSO4) Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkisi." Bartın Orman Fakültesi Dergisi, 19, ss.160 - 165, 2017.
ISNAD	TAN, Hüseyin vd. "Baritle Emprenyenin (BaSO4) Odunun Fiziksel ve Mekanik Özellikleri Üzerine Etkisi". Bartın Orman Fakültesi Dergisi 19/2 (2017), 160-165.