The Effects of Solid Particle Erosion of ZrN Coating Material on GF/EP and CF/EP Composites by Using PVD Method

Bagci, Mehmet

The Effects of Solid Particle Erosion of ZrN Coating Material on GF/EP and CF/EP Composites by Using PVD Method

Mehmet BAĞCI (Konya Selçuk Üniversitesi, Mühendislik Fakültesi, Makine Mühendisliği Bölümü, Konya, Türkiye)

Politeknik Dergisi

0 0

Yıl: 2019 Cilt: 22 Sayı: 1 Sayfa Aralığı: 87 - 93 Metin Dili: İngilizce İndeks Tarihi: 18-12-2019

The Effects of Solid Particle Erosion of ZrN Coating Material on GF/EP and CF/EP Composites by Using PVD Method

Öz:

Protective coatings produced by using Physical Vapour Deposition (PVD) method can increase the life time of the components. Therefore; in this study, ≈0.25 mm thickness ZrN coatings are applied on Glass Fiber Reinforced Epoxy (GF/EP) and Carbon Fiber Reinforced Epoxy (CF/EP) composites by magnetron sputtering to gain an improved understanding of the erosion resistance. The impingement angles used in the tests were 30°, 60° and 90°, while the impact velocity was 53 m/s. Al2O3 abrasive particles with an average diameter of 200 mm was used. All test specimens regardless of their various properties exhibit maximum erosion rates at 30° impingement angle and thus exhibiting similar behavior as that observed for ductile materials. Optic microscopic views were performed on the surfaces in order to characterize the erosion mechanism. The erodent particles of the both coating layer and composite matrix were found of main role in governing the wear progression. The measured erosion rates were sensitively correlated with the material removal process in order to explain the changes within the coated interfaces.

Anahtar Kelime:

Konular: Mühendislik, Elektrik ve Elektronik Bilgisayar Bilimleri, Yazılım Mühendisliği Mühendislik, Makine Mühendislik, Jeoloji Bilgisayar Bilimleri, Bilgi Sistemleri Bilgisayar Bilimleri, Donanım ve Mimari Mühendislik, Kimya

Belge Türü: Makale Makale Türü: Araştırma Makalesi Erişim Türü: Erişime Açık

[1] Srivastava V.K., “Effects of wheat starch on erosive wear of E-glass fiber reinforced epoxy resin composite materials”, Materials Science Engineering: A, 435-436: 282-287, (2006).
[2] Mohan N., Mahesha C. R., Rajaprakash B. M., “Erosive wear behaviour of WC filled glass epoxy composites”, Procedia Engineering, 68: 694-702, (2013).
[3] Yang L., Li H.L., Zhou Y.C., Zhu W., Wei Y.G., Zhang J.P.“Erosion failure mechanism of EB-PVD thermal barrier coatings with real morphology”, Wear, 392-393: 99-108, (2017).
[4] Rout A.K. and Satapathy A., “Study on mechanical and tribo-performance of rice-husk filled glass–epoxy hybrid composites”, Materials & Design, 41: 131-141, (2012).
[5] Mahapatra S.S., Patnaik A., “Study on mechanical and erosion wear behavior of hybrid composites using Taguchi experimental design”, Materials & Design, 30(8): 2791-2801, (2009).
[6] Bagci M., “Determination of solid particle erosion with Taguchi optimization approach of hybrid composite systems”, Tribology International, 94: 336-345, (2016).
[7] Shin D., Hamed A., “Influence of micro–structure on erosion resistance of plasma sprayed 7YSZ thermal barrier coating under gas turbine operating conditions”, Wear, 396-397: 34-47, (2018).
[8] Maurer C., Schulz U., “Solid particle erosion of thick PVD coatings on CFRP”, Wear, 317: 246-253, (2014).
[9] ASTM D3039 / D3039M-17, “Standard test method for tensile properties of polymer matrix composite materials”, ASTM International, West Conshohocken, PA, (2017). www.astm.org/cgi-bin/resolver.cgi?D3039D3039M-17
[10] ASTM D2583-13a, “Standard test method for indentation hardness of rigid plastics by means of a Barcol impressor”, ASTM International, West Conshohocken, PA, (2013). www.astm.org/cgi-bin/resolver.cgi?D2583-13a
[11] ASTM G76–95, “Standard test method for conducting erosion tests by solid particle impingement using gas jets”, ASTM International, West Conshohocken, PA, (2000). www.astm.org/cgi-bin/resolver.cgi?G76-95
[12] Ruff A. W., Ives L.K., “Measurement of solid particle velocity in erosive wear”, Wear, 35: 195-199, (1975).
[13] Finnie I., “Some reflections on the past and future of erosion”, Wear, 186-187(1): 1-10, (1995).
[14] G., Roy M., “Solid particle erosion behaviour of metallic materials at room and elevated temperatures”, Tribology International, 30(5): 339-359, (1997).
[15] Hutchings I.M., “Ductile-brittle transitions and wear maps for the erosion and abrasion of brittle material”, Journal of Physics D: Applied Physics, 25: 212-221, (1992).
[16] Bagci M., “Influence of fiber orientation on solid particle erosion of uni/multidirectional carbon fiber/glass fiber reinforced epoxy composites”, Proceedings of the Institution of Mechanical Engineers, Part J: Journal of Engineering Tribology, 231(5): 594-603, (2017).
[17] Azar G.T.P., Yelkarasi C., Ürgen M., “The role of droplets on the cavitation erosion damage of TiN coatings produced with cathodic arc physical vapor deposition”, Surface and Coatings Technology, 322: 211-217, (2017).

APA	Bagci M (2019). The Effects of Solid Particle Erosion of ZrN Coating Material on GF/EP and CF/EP Composites by Using PVD Method. , 87 - 93.
Chicago	Bagci Mehmet The Effects of Solid Particle Erosion of ZrN Coating Material on GF/EP and CF/EP Composites by Using PVD Method. (2019): 87 - 93.
MLA	Bagci Mehmet The Effects of Solid Particle Erosion of ZrN Coating Material on GF/EP and CF/EP Composites by Using PVD Method. , 2019, ss.87 - 93.
AMA	Bagci M The Effects of Solid Particle Erosion of ZrN Coating Material on GF/EP and CF/EP Composites by Using PVD Method. . 2019; 87 - 93.
Vancouver	Bagci M The Effects of Solid Particle Erosion of ZrN Coating Material on GF/EP and CF/EP Composites by Using PVD Method. . 2019; 87 - 93.
IEEE	Bagci M "The Effects of Solid Particle Erosion of ZrN Coating Material on GF/EP and CF/EP Composites by Using PVD Method." , ss.87 - 93, 2019.
ISNAD	Bagci, Mehmet. "The Effects of Solid Particle Erosion of ZrN Coating Material on GF/EP and CF/EP Composites by Using PVD Method". (2019), 87-93.

APA	Bagci M (2019). The Effects of Solid Particle Erosion of ZrN Coating Material on GF/EP and CF/EP Composites by Using PVD Method. Politeknik Dergisi, 22(1), 87 - 93.
Chicago	Bagci Mehmet The Effects of Solid Particle Erosion of ZrN Coating Material on GF/EP and CF/EP Composites by Using PVD Method. Politeknik Dergisi 22, no.1 (2019): 87 - 93.
MLA	Bagci Mehmet The Effects of Solid Particle Erosion of ZrN Coating Material on GF/EP and CF/EP Composites by Using PVD Method. Politeknik Dergisi, vol.22, no.1, 2019, ss.87 - 93.
AMA	Bagci M The Effects of Solid Particle Erosion of ZrN Coating Material on GF/EP and CF/EP Composites by Using PVD Method. Politeknik Dergisi. 2019; 22(1): 87 - 93.
Vancouver	Bagci M The Effects of Solid Particle Erosion of ZrN Coating Material on GF/EP and CF/EP Composites by Using PVD Method. Politeknik Dergisi. 2019; 22(1): 87 - 93.
IEEE	Bagci M "The Effects of Solid Particle Erosion of ZrN Coating Material on GF/EP and CF/EP Composites by Using PVD Method." Politeknik Dergisi, 22, ss.87 - 93, 2019.
ISNAD	Bagci, Mehmet. "The Effects of Solid Particle Erosion of ZrN Coating Material on GF/EP and CF/EP Composites by Using PVD Method". Politeknik Dergisi 22/1 (2019), 87-93.