Cyclic Fatigue Resistance of Biorace Nickel-titanium File withVariable Taper after Immersion in Sodium Hypochloride
Yıl: 2021 Cilt: 9 Sayı: 1 Sayfa Aralığı: 25 - 28 Metin Dili: İngilizce DOI: 10.14235/bas.galenos.2020.3918 İndeks Tarihi: 20-06-2021
Cyclic Fatigue Resistance of Biorace Nickel-titanium File withVariable Taper after Immersion in Sodium Hypochloride
Öz: Objective: This study aimed to evaluate the effect of sodium hypochlorite on the cyclic fatigue resistance of BioRace (BR) files according to taper.Methods: BR 25.04 and 25.06 files were divided into the following groups: group 1, 20 BR 25.04 with no immersion in NaOCl; group 2, 20 BR 25.04 with immersion in 5.25% NaOCl at 37 °C ±1 °C for 5 min; group 3, 20 BR 25.06 with no immersion; and group 4, 20 BR 25.06 with immersion in 5.25% NaOCl at 37 °C ±1 °C for 5 min. The instruments were applied to a stainless-steel artificial root canal of 60° curvature and 5-mm radius. The time to failure (TTF) in seconds and number of cycles to failure (NCF) were recorded.Results: The cyclic fatigue resistance of BR 25.04 was significantly higher than that of BR 25.06. The TTF and NCF values were significantly higher in group 1 than in groups 2 and 3 and in group 2 than in group 4. However, neither value differed significantly between groups 3 and 4 (p>0.05).Conclusion: Taper and sodium hypochlorite affected the cyclic fatigue resistance of BR.
Anahtar Kelime: Sodyum Hipokloritin Farklı Taperlardaki Biorace Nikel Titanyum Eğesinin Döngüsel Yorgunluk Direncine Etkisinin Değerlendirilmesi
Öz: Amaç: Bu çalışmanın amacı sodyum hipokloridin farklı taperlarasahip olan BioRace (BR) döner alet sisteminin döngüselyorgunluğuna etkisini değerlendirmektir. Yöntemler: BR 25,04 ve BR 25,06 enstrümanlarının döngüselyorgunlukları, farklı koşullarda test edildi. Grup 1, BR 25,04 nolueğe hiç bir solüsyonda bekletilmeden; grup 2: BR 25,04 %5,25NaOCl solüsyonunda 37 °C ±1 °C’de 5 dakika bekletilerek; grup3: BR 25,06 hiç bir solüsyonda bekletilmeden; grup 4: BR 25,06%5,25 NaOCl solüsyonunda 37 °C ±1 °C’de 5 dakika bekletildiktensonra 60° kurvatür açılı and 5 mm kurvatür yarıçaplı paslanmazçelik bloktan üretilmiş eğimli olukta test edildi. Her bir eğeninkırılana kadarki döngü sayısı (NCF) ve kırılana kadarki süresi(TTF) saniye cinsinden kaydedildi. Elde edilen veriler istatistikselanalizler ile değerlendirildi. Bulgular: BR 25,04 eğesinin döngüsel yorgunluk direnci, BR25,06’dan istatistiksel olarak daha yüksektir. TTF ve NCF değerlerigrup 1 > grup 2 , grup 1 > grup 3 , grup 2 > grup 4 şeklindebulundu. Buna karşılık, grup 3 ve grup 4 arasında istatistiksel olarakanlamlı bir fark yoktu. Sonuç: Bu çalışmanın sınırları doğrultusunda BR ensturmanlarınıntaperı ve sodyum hipokloritte bekletilmesi aletin döngüselyorgunluğuna etki etmektedir.
Anahtar Kelime: Belge Türü: Makale Makale Türü: Araştırma Makalesi Erişim Türü: Erişime Açık
- 1. Cheung GSP. Instrument fracture: mechanisms, removal of fragments and clinical outcomes. Endod Topics 2007;16:1-26.
- 2. Elnaghy AM, Elsaka SE. Effect of sodium hypochlorite and saline on cyclic fatigue resistance of WaveOne Gold and Reciproc reciprocating instruments. Int Endod J 2017;50:991-8.
- 3. Ertuğrul IF, Orhan EO. Cyclic fatigue and energy dispersive X-ray spectroscopy examination of the novel ROTATE instrument. Microsc Res Tech 2019;1-7.
- 4. Lopes HP, Elias CN, Vieira VT, Moreira EJ, Marques RV, de Oliveira JC, et al. Effects of electropolishing surface treatment on the cyclic fatigue resistance of BioRace nickel-titanium rotary instruments. J Endod 2010;36:1653-7.
- 5. Freire LG, Gavini G, Branco-Barletta F, Sanches-Cunha R, dos Santos M. Microscopic computerized tomographic evaluation of root canal transportation prepared with twisted or ground nickel-titanium rotary instruments. Oral Surg Oral Med Oral Pathol Oral Radiol Endod 2011:112;143-8.
- 6. FKG. BioRace brochure. Available at: https://www.fkg.ch/sites/ default/files/fkg_br_brochure_an_lowr.pdf. Accessed at 20.11.2019.
- 7. Gambarini G, Grande NM, Plotino G, Somma F, Garala M, De Luca M, et al. Fatigue resistance of engine-driven rotary nickel- titanium instruments produced by new manufacturing methods. J Endod 2008:34;1003-5.
- 8. O’Hoy PY, Messer HH, Palamara JE. The effect of cleaning procedures on fracture properties and corrosion of NiTi files. Int Endod J 2003;36:724-32.
- 9. Darabara M, Bourithis L, Zinelis S, Papadimitriou GD. Susceptibility to localized corrosion of stainless steel and NiTi endodontic instruments in irrigating solutions. Int Endod J 2004;37:705-10.
- 10. Berutti E, Angelini E, Rigolone M, Migliaretti G, Pasqualini D. Influence of sodium hypochlorite on fracture properties and corrosion of ProTaper Rotary instruments. Int Endod J 2006;39:693-9.
- 11. Haikel Y, Serfaty R, Wilson P, Speisser JM, Allemann C. Mechanical properties of nickeltitanium endodontic instruments and the effect of sodium hypochlorite treat- ment. J Endod 1998;24:731-5.
- 12. Pedulla E, Grande N, Plotino G, Pappalardo A, Rapisarda E. Cyclic Fatigue Resistance of Three Different Nickel-Titanium Instruments after Immersion in Sodium Hypochlorite. J Endod 2011;37:1139- 42.
- 13. Kim HC, Kwak SW, Shun-Pan Cheung G, Ko DH, Chung S, Lee W. Cyclic Fatigue and Torsional Resistance of Two New Nickel-Titanium Instruments Used in Reciprocation Motion: Reciproc Versus WaveOne. J Endod 2012;38:541-4.
- 14. Sattapan B, Nervo GJ, Palamara JE, Messer HH. Defects in rotary nickel-titanium files after clinical use. J Endod 2000;26:161-5.
- 15. Karataş E, Arslan H, Büker M, Seçkin F, Çapar ID. Effect of movement kinematics on the cyclic fatigue resistance of nickel-titanium instruments. Int Endod J 2016;49:361-4.
- 16. Schrader C, Peters OA. Analysis of torque and force with differently tapered rotary endodontic instruments in vitro. J Endod 2005;31:120- 3.
- 17. Barbosa F, gomes J, De araújo M. Influence of previous angular deformation on flexural fatigue resistance of K3 nickel- titanium rotary instruments. J Endod 2007;33:1477-80.
- 18. Saber SMS, Seeda MMA, Hassanien E. The effect of instrument material, taper and degree of root canal curvature on cyclic fatigue of rotary nickel-titanium instruments. ENDO (Lond Engl) 2013;7:59- 64
- 19. Pruett JP, Clement DJ, Carnes DL. Cyclic fatigue testing of nickel titanium instruments. J Endod 1997;23:77-85.
- 20. Topçuoğlu HS, Pala K, Aktı A, Düzgün S, Topçuoğlu G. Cyclic fatigue resistance of D-RaCe, ProTaper, and Mtwo nickel–titanium retreatment instruments after immersion in sodium hypochlorite. Clin Oral Invest 2016;20:1175-9.
- 21. Nguyen HH, Fong H, Paranjpe A, Flake NM, Johnson JD, Peters OA. Evaluation of the resistance to cyclic fatigue between ProTaper Next, ProTaper Universal, and Vortex Blue rotary instruments. J Endod 2014;40:1190-3.
| APA | Arıcan B, ATAV ATEŞ A (2021). Cyclic Fatigue Resistance of Biorace Nickel-titanium File withVariable Taper after Immersion in Sodium Hypochloride. , 25 - 28. 10.14235/bas.galenos.2020.3918 |
| Chicago | Arıcan Burçin,ATAV ATEŞ Ayfer Cyclic Fatigue Resistance of Biorace Nickel-titanium File withVariable Taper after Immersion in Sodium Hypochloride. (2021): 25 - 28. 10.14235/bas.galenos.2020.3918 |
| MLA | Arıcan Burçin,ATAV ATEŞ Ayfer Cyclic Fatigue Resistance of Biorace Nickel-titanium File withVariable Taper after Immersion in Sodium Hypochloride. , 2021, ss.25 - 28. 10.14235/bas.galenos.2020.3918 |
| AMA | Arıcan B,ATAV ATEŞ A Cyclic Fatigue Resistance of Biorace Nickel-titanium File withVariable Taper after Immersion in Sodium Hypochloride. . 2021; 25 - 28. 10.14235/bas.galenos.2020.3918 |
| Vancouver | Arıcan B,ATAV ATEŞ A Cyclic Fatigue Resistance of Biorace Nickel-titanium File withVariable Taper after Immersion in Sodium Hypochloride. . 2021; 25 - 28. 10.14235/bas.galenos.2020.3918 |
| IEEE | Arıcan B,ATAV ATEŞ A "Cyclic Fatigue Resistance of Biorace Nickel-titanium File withVariable Taper after Immersion in Sodium Hypochloride." , ss.25 - 28, 2021. 10.14235/bas.galenos.2020.3918 |
| ISNAD | Arıcan, Burçin - ATAV ATEŞ, Ayfer. "Cyclic Fatigue Resistance of Biorace Nickel-titanium File withVariable Taper after Immersion in Sodium Hypochloride". (2021), 25-28. https://doi.org/10.14235/bas.galenos.2020.3918 |
| APA | Arıcan B, ATAV ATEŞ A (2021). Cyclic Fatigue Resistance of Biorace Nickel-titanium File withVariable Taper after Immersion in Sodium Hypochloride. Bezmiâlem Science, 9(1), 25 - 28. 10.14235/bas.galenos.2020.3918 |
| Chicago | Arıcan Burçin,ATAV ATEŞ Ayfer Cyclic Fatigue Resistance of Biorace Nickel-titanium File withVariable Taper after Immersion in Sodium Hypochloride. Bezmiâlem Science 9, no.1 (2021): 25 - 28. 10.14235/bas.galenos.2020.3918 |
| MLA | Arıcan Burçin,ATAV ATEŞ Ayfer Cyclic Fatigue Resistance of Biorace Nickel-titanium File withVariable Taper after Immersion in Sodium Hypochloride. Bezmiâlem Science, vol.9, no.1, 2021, ss.25 - 28. 10.14235/bas.galenos.2020.3918 |
| AMA | Arıcan B,ATAV ATEŞ A Cyclic Fatigue Resistance of Biorace Nickel-titanium File withVariable Taper after Immersion in Sodium Hypochloride. Bezmiâlem Science. 2021; 9(1): 25 - 28. 10.14235/bas.galenos.2020.3918 |
| Vancouver | Arıcan B,ATAV ATEŞ A Cyclic Fatigue Resistance of Biorace Nickel-titanium File withVariable Taper after Immersion in Sodium Hypochloride. Bezmiâlem Science. 2021; 9(1): 25 - 28. 10.14235/bas.galenos.2020.3918 |
| IEEE | Arıcan B,ATAV ATEŞ A "Cyclic Fatigue Resistance of Biorace Nickel-titanium File withVariable Taper after Immersion in Sodium Hypochloride." Bezmiâlem Science, 9, ss.25 - 28, 2021. 10.14235/bas.galenos.2020.3918 |
| ISNAD | Arıcan, Burçin - ATAV ATEŞ, Ayfer. "Cyclic Fatigue Resistance of Biorace Nickel-titanium File withVariable Taper after Immersion in Sodium Hypochloride". Bezmiâlem Science 9/1 (2021), 25-28. https://doi.org/10.14235/bas.galenos.2020.3918 |