Experimental Investigation of Dry Environment Abrasive Wear Behavior of a Plain Bearing Material

Demirsöz, Recep

doi:10.30855/gmbd.2022.01.08

Experimental Investigation of Dry Environment Abrasive Wear Behavior of a Plain Bearing Material

Recep Demirsöz (Karabük Üniversitesi, Mühendislik Fakültesi, Makine Mühendisliği Bölümü, Karabük, Türkiye)

Gazi Mühendislik Bilimleri Dergisi

4 0

Yıl: 2022 Cilt: 8 Sayı: 1 Sayfa Aralığı: 89 - 102 Metin Dili: İngilizce DOI: 10.30855/gmbd.2022.01.08 İndeks Tarihi: 29-07-2022

Experimental Investigation of Dry Environment Abrasive Wear Behavior of a Plain Bearing Material

Öz:

In this study, using variables such as load and sliding speed, which are effective parameters on abrasive wear, the amount of wear on the bearing material, friction coefficients, and trace depth values according to the experimental conditions were determined. According to the results of the analysis of variance performed as a result of the experiments carried out in the ball-on-flat experimental setup, the most effective parameter for all outputs was the load value, and the effect ratio for mass loss was 66.26%, the effect ratio for the friction coefficient was 53.02% and the effect ratio for the trace depth was 85.69%. The R2 values obtained from the comparison of the experimental results with the regression results were found to be 0.9750, 0.9988, and 0.9759 for mass loss, friction coefficient, and trace depth, respectively. These results show that the regression model fit is good.

Anahtar Kelime: dry sliding Abrasive wear bearing material ANOVA

Bir Kaymalı Yatak Malzemesinin Kuru Ortam Abrazif Aşınma Davranışının Deneysel Olarak İncelenmesi

Öz:

Bu çalışmada, abrazif aşınma konusunda etkili parametreler olan yük ve kayma hızı gibi değişkenler kullanılarak yatak malzemesinde meydana gelen aşınma miktarları, deney şartlarına göre sürtünme katsayıları ve iz derinliği değerleri belirlenmiştir. Ball-on-flat deney düzeneğinde gerçekleştirilen deneyler sonucunda yapılan varyans analizi sonuçlarına göre tüm çıktılar için en etkili parametre yük değeri olup kütle kaybı için etki oranı %66,261, sürtünme katsayısı için etki oranı %53,021 ve iz derinliği için etki oranı ise %85,688 olarak bulunmuştur. Deneysel sonuçların regresyon sonuçları ile mukayesesinden elde edilen R2 değerleri ise kütle kaybı, sürtünme katsayısı ve iz derinliği için sırası ile 0,9750, 0,9988 ve 0,9759 olarak bulunmuştur. Bu sonuçlar regresyon model uyumunun iyi olduğunu göstermektedir.

Anahtar Kelime: ANOVA

Belge Türü: Makale Makale Türü: Araştırma Makalesi Erişim Türü: Erişime Açık

[1] E. De Robertis, E.H.H. Cosme, R.S. Neves, A.Y. Kuznetsov, A.P.C. Campos and S.M. Landi, “Application of the modulated temperature differential scanning calorimetry technique for the determination of the specific heat of copper nanofluids,” Applied Thermal Engineering, vol. 41, pp. 10–17, 2012. doi:10.1016/j.applthermaleng.2012.01.003.
[2] S. M. S. Murshed, “Determination of effective specific heat of nanofluids,” Journal of Experimental Nanoscience, vol. 6 no. 5, pp. 539–546, 2011. doi:10.1080/17458080.2010.498838.
[3] M. H. Cetin and S. Korkmaz, “Investigation of the concentration rate and aggregation behaviour of nano-silver added colloidal suspensions on wear behaviour of metallic materials by using ANOVA method,” Tribology International, vol. 147, pp. 106273, 2020. doi:10.1016/j.triboint.2020.106273.
[4] R. A. García-León, J. Martínez-Trinidad, R. Zepeda-Bautista, I. Campos-Silva, A. Guevara-Morales, J. Martínez-Londoño and J. Barbosa-Saldaña, “Dry sliding wear test on borided AISI 316L stainless steel under ball-on-flat configuration: A statistical analysis,” Tribology International, vol. 157, 2021. doi:10.1016/j.triboint.2021.106885.
[5] A. N. Sudhakar, R. Markandeya, B. Srinivasa Rao, Ajoy Kumar Pandey and D. Kaushik, “Effect of alloying elements on the dry sliding wear behavior of high chromium white cast iron and Ni-hard iron,” Materials Today: Proceedings, 2021. doi:10.1016/j.matpr.2021.09.295.
[6] Elleuch, Khaled, Riadh Elleuch, Ridha Mnif, Vincent Fridrici, and Philippe Kapsa, “Sliding Wear Transition for the CW614 Brass Alloy,” Tribology International vol. 39 no. 4, pp. 290–96, 2006. doi:10.1016/j.triboint.2005.01.036.
[7] Mindivan, H., H. Çimenoǧlu, and E. S. Kayali, “Microstructures and Wear Properties of Brass Synchroniser Rings,” Wear vol. 254, no. 5–6, pp. 532–37, 2003. doi:10.1016/S0043-1648(03)00023-1.
[8] L. Xu, Y. Zhang, D. Zhang and M. Leng, “Preparation and tribological properties of Ag nanoparticles/reduced graphene oxide nanocomposites,” Industrial Lubrication and Tribology, vol. 70, pp. 1684–1691, 2017. doi:10.1108/ILT-03-2017-0054.
[9] G. Pitchayyapillai, P. Seenikannan, P. Balasundar and P. Narayanasamy, “Effect of nanosilver on microstructure, mechanical and tribological properties of cast 6061 aluminum alloy,” Transactions of Nonferrous Metals Society of China, vol. 27, pp. 2137– 2145, 2017. doi:10.1016/S1003-6326(17)60239-5.
[10] H. Ghaednia, M.S. Hossain and R.L. Jackson, “Tribological Performance of Silver Nanoparticle–Enhanced Polyethylene Glycol Lubricants,” Tribology Transactions, vol. 59, pp. 585–592, 2016. doi:10.1080/10402004.2015.1092623.
[11] L. Gara and Q. Zou, “Friction and wear characteristics of oil-based ZnO nanofluids,” Tribology Transactions, vol. 56, pp. 236– 244, 2013. doi:10.1080/10402004.2012.740148.
[12] H. Xie, B. Jiang, J. He, X. Xia and F. Pan, “Lubrication performance of MoS2 and SiO2 nanoparticles as lubricant additives in magnesium alloy-steel contacts,” Tribology International, vol. 93, pp. 63–70, 2016. doi: 10.1016/j.triboint.2015.08.009.
[13] Y. Y. Wu, W. C. Tsui and T. C. Liu, “Experimental analysis of tribological properties of lubricating oils with nanoparticle additives,” Wear, vol. 262, pp. 819–825, 2007. doi: 10.1016/j.wear.2006.08.021.
[14] N. Yalçın, Y. Kayır ve S. Erkal, “AA2024 Alüminyum Alaşımına Uygulanan Yaşlandırma Yöntemlerinin İşlenebilirliğe Etkisinin Taguchi ve Anova ile Araştırılması,” Journal of Polytechnic, cilt 20, sayı 4, ss. 743–51, 2017. doi:10.2339/politeknik.368552.
[15] E. Nas, E. Zurnacı ve S. Yıldırım, “Sertleştirilmiş AISI H13 Takım Çeliğinin Delme Performansını İyileştirmek İçin Elektro Erozyon İşleme Parametrelerinin Taguchi Yöntemi Kullanılarak Modellenmesi ve Optimizasyonu,” Gazi Journal of Engineering Sciences, cilt 7, sayı 2, ss. 99–110, 2021. doi:10.30855/gmbd.2021.02.03.
[16] B. Özlü, M. Akgün ve H. Demir, “AA 6061 Alaşımının Tornalanmasında Kesme Parametrelerinin Yüzey Pürüzlülüğü Üzerine Etkisinin Analizi ve Optimizasyonu,” Gazi J. Eng. Sci., cilt 5, sayı 2, ss. 151–158, 2019. doi:10.30855/gmbd.2019.02.04.
[17] B. Kondul, “Borlama ile yüzeyi sertleştirilmiş ray çeliğinin aşınma davranışının incelenmesi,” Yüksek Lisans Tezi, KBÜ, Karabük, Türkiye, 2020.

APA	Demirsöz R (2022). Experimental Investigation of Dry Environment Abrasive Wear Behavior of a Plain Bearing Material. , 89 - 102. 10.30855/gmbd.2022.01.08
Chicago	Demirsöz Recep Experimental Investigation of Dry Environment Abrasive Wear Behavior of a Plain Bearing Material. (2022): 89 - 102. 10.30855/gmbd.2022.01.08
MLA	Demirsöz Recep Experimental Investigation of Dry Environment Abrasive Wear Behavior of a Plain Bearing Material. , 2022, ss.89 - 102. 10.30855/gmbd.2022.01.08
AMA	Demirsöz R Experimental Investigation of Dry Environment Abrasive Wear Behavior of a Plain Bearing Material. . 2022; 89 - 102. 10.30855/gmbd.2022.01.08
Vancouver	Demirsöz R Experimental Investigation of Dry Environment Abrasive Wear Behavior of a Plain Bearing Material. . 2022; 89 - 102. 10.30855/gmbd.2022.01.08
IEEE	Demirsöz R "Experimental Investigation of Dry Environment Abrasive Wear Behavior of a Plain Bearing Material." , ss.89 - 102, 2022. 10.30855/gmbd.2022.01.08
ISNAD	Demirsöz, Recep. "Experimental Investigation of Dry Environment Abrasive Wear Behavior of a Plain Bearing Material". (2022), 89-102. https://doi.org/10.30855/gmbd.2022.01.08

APA	Demirsöz R (2022). Experimental Investigation of Dry Environment Abrasive Wear Behavior of a Plain Bearing Material. Gazi Mühendislik Bilimleri Dergisi, 8(1), 89 - 102. 10.30855/gmbd.2022.01.08
Chicago	Demirsöz Recep Experimental Investigation of Dry Environment Abrasive Wear Behavior of a Plain Bearing Material. Gazi Mühendislik Bilimleri Dergisi 8, no.1 (2022): 89 - 102. 10.30855/gmbd.2022.01.08
MLA	Demirsöz Recep Experimental Investigation of Dry Environment Abrasive Wear Behavior of a Plain Bearing Material. Gazi Mühendislik Bilimleri Dergisi, vol.8, no.1, 2022, ss.89 - 102. 10.30855/gmbd.2022.01.08
AMA	Demirsöz R Experimental Investigation of Dry Environment Abrasive Wear Behavior of a Plain Bearing Material. Gazi Mühendislik Bilimleri Dergisi. 2022; 8(1): 89 - 102. 10.30855/gmbd.2022.01.08
Vancouver	Demirsöz R Experimental Investigation of Dry Environment Abrasive Wear Behavior of a Plain Bearing Material. Gazi Mühendislik Bilimleri Dergisi. 2022; 8(1): 89 - 102. 10.30855/gmbd.2022.01.08
IEEE	Demirsöz R "Experimental Investigation of Dry Environment Abrasive Wear Behavior of a Plain Bearing Material." Gazi Mühendislik Bilimleri Dergisi, 8, ss.89 - 102, 2022. 10.30855/gmbd.2022.01.08
ISNAD	Demirsöz, Recep. "Experimental Investigation of Dry Environment Abrasive Wear Behavior of a Plain Bearing Material". Gazi Mühendislik Bilimleri Dergisi 8/1 (2022), 89-102. https://doi.org/10.30855/gmbd.2022.01.08