Effects of coloring procedures on shear bond strength between resin cement and colored zirconia
Yıl: 2018 Cilt: 52 Sayı: 3 Sayfa Aralığı: 122 - 126 Metin Dili: İngilizce DOI: 10.26650/eor.2018.440 İndeks Tarihi: 30-06-2020
Effects of coloring procedures on shear bond strength between resin cement and colored zirconia
Öz: Debonding is expected as a frequent failure type in zirconia restorations. Thereforethe aim of the current study is to evaluate the shear bond strength between coloredzirconia and resin cement.Materials and methodsThere were 11 groups evaluated each containing 12 zirconia discs (15 mm x 12 mmx 1.6 mm). Groups were colored with the colors A3, B1, C4, D2, and D4 of the VITAclassical shade scale. Coloring procedure was carried out for either 3 second or 60seconds for the study groups and the control group was left untreated. Specimenswere then bonded to translucent resin cement having a thickness of 3 mm and widthof 3 mm. The shear bond strength of the samples was measured in a universal testingmachine with a crosshead speed of 1 mm per minute. Two-way analysis of varianceand Tukey’s HSD test were used for pairwise comparisons. Also paired t-test was usedfor comparing groups with the same color but having different shading times.ResultsAny significant difference was not found between the shear bond strengths ofsamples depending on whether color or shading times. Among the groups, B1 (60seconds of coloring) had the highest bond strength (10.05 MPa), while A3 (60 secondsof coloring) showed the lowest bond strength (6.72 MPa). However, these differenceswere not statistically significant.ConclusionColoring zirconia did not affect the shear bond strength between zirconia and resincement.
Anahtar Kelime: .
Öz: Renklendirme süreçlerinin zirkonya ile rezin siman arasındaki bağlanma dayanımı üzerindeki etkileri. Amaç: Desimantasyon zirkonya destekli restorasyonlar için sık görülen sorunlarından biridir. Bu çalışmanın amacı, renklendirilmiş zirkonyum oksit alt yapı ile rezin siman ile arasındaki makaslama bağlanma dayanımını incelemektir. Gereç ve Yöntem: Her birinde 12 zirkonya disk (15 mm x 12 mm x 1.6 mm) olacak şekilde 11 grup oluşturulmuştur. Gruplar VITA klasik renk skalasına göre: A3, B1, C4, D2 ve D4 renklerine uyumlu olarak renklendirilmiştir. Tüm gruplara önerilen 3 saniyelik renklendirme ve 60 saniyelik uzatılmış renklendirme işlemi uygulanmıştır. Kontrol grubunda renklendirme yapılmamıştır. Örneklere 3 mm kalınlığında ve 3 mm yüksekliğinde translusent rezin siman uygulanmış ve üniversal test cihazında 1 mm/dakika hızında bağlanma dayanımı testi yapılmıştır. İki yönlü varyans analizi (ANOVA) ve ikili karşılaştırmalarda Tukey HSD testi kullanılmıştır. Aynı renkte olan ancak farklı tonlama süresine maruz kalan örnekler ise t-testi ile değerlendirilmiştir. Bulgular: Makaslama bağlantı dayanımının renk ya da renklendirme sürelerine bağlı olarak anlamlı bir fark göstermediği belirlenmiştir. 11 araştırma grubunun içinde en yüksek bağlantı değeri (10,05 MPa) 60 saniye renklendirme uygulanan B1 renk grubunda; en düşük bağlantı değeri (6,72 Mpa), 60 saniye renklendirme uygulanan A3 renk grubunda elde edilmiştir. Ancak bu farklar istatistiksel olarak anlamlı değildir. Sonuç: Zirkonya alt yapı ve rezin siman arası bağlantı dayanımı zirkonyayı renklendirme işlemlerinden etkilenmemektedir. Anahtar kelimeler: Makaslama bağlanma dayanımı; seramik; renklendirme; zirkonya; rezin siman
Anahtar Kelime: Belge Türü: Makale Makale Türü: Araştırma Makalesi Erişim Türü: Erişime Açık
- 1. Tinschert J, Zwez D, Marx R, Anusavice KJ. Structural reliability of alumina-, feldspar-, leucite-, mica- and zirconia-based ceramics. J Dent 2000; 28: 529-35. [CrossRef]
- 2. Ardlin BI. Transformation-toughened zirconia for dental inlays, crowns and bridges: Chemical stability and effect of low-temperature aging on flexural strength and surface structure. Dent Mater 2002; 18: 590-5. [CrossRef]
- 3. Ichikawa Y, Akagawa Y, Nikai H, Tsuru H. Tissue compatibility and stability of a new zirconia ceramic in vivo. J Prosthet Dent 1992; 68: 322-6. [CrossRef]
- 4. Piconi C, Maccauro G. Zirconia as a ceramic biomaterial. Biomaterials 1999; 20: 1-25. [CrossRef]
- 5. Oilo M, Gjerdet NR, Tvinnereim HM. The firing procedure influences properties of a zirconia core ceramic. Dent Mater 2008; 24: 471-5. [CrossRef]
- 6. Blatz MB, Oppes S, Chiche G, Holst S, Sadan A. Influence of cementation technique on fracture strength and leakage of alumina all-ceramic crowns after cyclic loading. Quintessence Int 2008; 39: 23-32.
- 7. Blatz MB, Sadan A, Kern M. Resin-ceramic bonding: A review of the literature. J Prosthet Dent 2003; 89: 268-74. [CrossRef]
- 8. Atsu SS, Kilicarslan MA, Kucukesmen HC, Aka PS. Effect of zirconium-oxide ceramic surface treatments on the bond strength to adhesive resin. J Prosthet Dent 2006; 95: 430-6. [CrossRef]
- 9. Derand T, Molin M, Kvam K. Bond strength of composite luting cement to zirconia ceramic surfaces. Dent Mater 2005; 21: 1158-62. [CrossRef]
- 10. Palacios RP, Johnson GH, Phillips KM, Raigrodski AJ. Retention of zirconium oxide ceramic crowns with three types of cement. J Prosthet Dent 2006; 96: 104-14. [CrossRef]
- 11. Chang J, Da Silva JD, Sakai M, Kristiansen J, Ishikawa-Nagai S. The optical effect of composite luting cement on all ceramic crowns. J Dent 2009; 37: 937-43. [CrossRef]
- 12. Hill EE. Dental cements for definitive luting: A review and practical clinical considerations. Dent Clin North Am 2007; 51: 643-58. [CrossRef]
- 13. Blatz MB, Sadan A, Maltezos C, Blatz U, Mercante D, Burgess JO. In vitro durability of the resin bond to feldspathic ceramics. Am J Dent 2004; 17: 169-72.
- 14. Kern M, Wegner SM. Bonding to zirconia ceramic: Adhesion methods and their durability. Dent Mater 1998; 14: 64-71. [CrossRef]
- 15. Luthy H, Loeffel O, Hammerle CH. Effect of thermocycling on bond strength of luting cements to zirconia ceramic. Dent Mater 2006; 22: 195-200. [CrossRef] Coloring procedures and bond strength 125
- 16. Lohbauer U, Zipperle M, Rischka K, Petschelt A, Muller FA. Hydroxylation of dental zirconia surfaces: Characterization and bonding potential. J Biomed Mater Res B Appl Biomater 2008; 87: 461-7. [CrossRef]
- 17. Aboushelib MN, de Jager N, Kleverlaan CJ, Feilzer AJ. Microtensile bond strength of different components of core veneered all-ceramic restorations. Dent Mater 2005; 21: 984-91. [CrossRef]
- 18. Stevenson B, Ibbetson R. The effect of the substructure on the colour of samples/restorations veneered with ceramic: A literature review. J Dent 2010; 38: 361-8. [CrossRef]
- 19. Deville S, Gremillard L, Chevalier J, Fantozzi G. A critical comparison of methods for the determination of the aging sensitivity in biomedical grade yttria-stabilized zirconia. J Biomed Mater Res B Appl Biomater 2005; 72: 239-45. [CrossRef]
- 20. Hjerppe J, Narhi T, Froberg K, Vallittu PK, Lassila LV. Effect of shading the zirconia framework on biaxial strength and surface microhardness. Acta Odontol Scand 2008 ;66: 262-7. [CrossRef]
- 21. Pittayachawan P, McDonald A, Petrie A, Knowles JC. The biaxial flexural strength and fatigue property of lava y-tzp dental ceramic. Dent Mater 2007; 23: 1018-29. [CrossRef]
- 22. Aboushelib MN, Kleverlaan CJ, Feilzer AJ. Effect of zirconia type on its bond strength with different veneer ceramics. J Prosthodont 2008; 17: 401-8. [CrossRef]
- 23. Mosharraf R, Rismanchian M, Savabi O, Ashtiani AH. Influence of surface modification techniques on shear bond strength between different zirconia cores and veneering ceramics. J Adv Prosthodont 2011; 3: 221-8. [CrossRef]
- 24. Chevalier J, Deville S, Munch E, Jullian R, Lair F. Critical effect of cubic phase on aging in 3mol% yttria-stabilized zirconia ceramics for hip replacement prosthesis. Biomaterials 2004; 25: 5539- 45. [CrossRef]
- 25. Chen PL, Chen IW. Grain boundary mobility in y2o3: Defect mechanism and dopant effects. J Am Ceram Soc 1996; 79: 1801- 9. [CrossRef]
- 26. Blackman R, Barghi N, Duke E. Influence of ceramic thickness on the polymerization of light-cured resin cement. J Prosthet Dent 1990; 63: 295-300. [CrossRef]
- 27. Hasegawa EA, Boyer DB, Chan DC.
- 16. Lohbauer U, Zipperle M, Rischka K, Petschelt A, Muller FA. Hydroxylation of dental zirconia surfaces: Characterization and bonding potential. J Biomed Mater Res B Appl Biomater 2008; 87: 461-7. [CrossRef]
- 17. Aboushelib MN, de Jager N, Kleverlaan CJ, Feilzer AJ. Microtensile bond strength of different components of core veneered all-ceramic restorations. Dent Mater 2005; 21: 984-91. [CrossRef]
- 18. Stevenson B, Ibbetson R. The effect of the substructure on the colour of samples/restorations veneered with ceramic: A literature review. J Dent 2010; 38: 361-8. [CrossRef]
- 19. Deville S, Gremillard L, Chevalier J, Fantozzi G. A critical comparison of methods for the determination of the aging sensitivity in biomedical grade yttria-stabilized zirconia. J Biomed Mater Res B Appl Biomater 2005; 72: 239-45. [CrossRef]
- 20. Hjerppe J, Narhi T, Froberg K, Vallittu PK, Lassila LV. Effect of shading the zirconia framework on biaxial strength and surface microhardness. Acta Odontol Scand 2008 ;66: 262-7. [CrossRef]
- 21. Pittayachawan P, McDonald A, Petrie A, Knowles JC. The biaxial flexural strength and fatigue property of lava y-tzp dental ceramic. Dent Mater 2007; 23: 1018-29. [CrossRef]
- 22. Aboushelib MN, Kleverlaan CJ, Feilzer AJ. Effect of zirconia type on its bond strength with different veneer ceramics. J Prosthodont 2008; 17: 401-8. [CrossRef]
- 23. Mosharraf R, Rismanchian M, Savabi O, Ashtiani AH. Influence of surface modification techniques on shear bond strength between different zirconia cores and veneering ceramics. J Adv Prosthodont 2011; 3: 221-8. [CrossRef]
- 24. Chevalier J, Deville S, Munch E, Jullian R, Lair F. Critical effect of cubic phase on aging in 3mol% yttria-stabilized zirconia ceramics for hip replacement prosthesis. Biomaterials 2004; 25: 5539- 45. [CrossRef]
- 25. Chen PL, Chen IW. Grain boundary mobility in y2o3: Defect mechanism and dopant effects. J Am Ceram Soc 1996; 79: 1801- 9. [CrossRef]
- 26. Blackman R, Barghi N, Duke E. Influence of ceramic thickness on the polymerization of light-cured resin cement. J Prosthet Dent 1990; 63: 295-300. [CrossRef]
- 27. Hasegawa EA, Boyer DB, Chan DC. Hardening of dual-cured cements under composite resin inlays. J Prosthet Dent 1991; 66: 187-92. [CrossRef]
- 28. Warren K. An investigation into the microhardness of a light cured composite when cured through varying thicknesses of porcelain. J Oral Rehabil 1990; 17: 327-34. [CrossRef]
- 29. Heffernan MJ, Aquilino SA, Diaz-Arnold AM, Haselton DR, Stanford CM, Vargas MA. Relative translucency of six all-ceramic systems. Part I: Core materials. J Prosthet Dent 2002; 88: 4-9. [CrossRef]
- 30. Moon JE, Kim SH, Lee JB, Ha SR, Choi YS. The effect of preparation order on the crystal structure of yttria-stabilized tetragonal zirconia polycrystal and the shear bond strength of dental resin cements. Dent Mater 2011; 27: 651-63. [CrossRef]
- 31. Kim MJ, Kim YK, Kim KH, Kwon TY. Shear bond strengths of various luting cements to zirconia ceramic: Surface chemical aspects. J Dent 2011; 39: 795-803. [CrossRef]
- 32. Komine F, Kobayashi K, Saito A, Fushiki R, Koizumi H, Matsumura H. Shear bond strength between an indirect composite veneering material and zirconia ceramics after thermocycling. J Oral Sci 2009; 51: 629-34. [CrossRef]
- 33. Kuriyama S, Terui Y, Higuchi D, Goto D, Hotta Y, Manabe A, Miyazaki T. Novel fabrication method for zirconia restorations: Bonding strength of machinable ceramic to zirconia with resin cements. Dent Mater J 2011; 30: 419-24. [CrossRef]
- 34. Lin J, Shinya A, Gomi H, Shinya A. Effect of self-adhesive resin cement and tribochemical treatment on bond strength to zirconia. Int J Oral Sci 2010; 2: 28-34. [CrossRef]
- 35. Takeuchi K, Fujishima A, Manabe A, Kuriyama S, Hotta Y, Tamaki Y, Miyazaki T. Combination treatment of tribochemical treatment and phosphoric acid ester monomer of zirconia ceramics enhances the bonding durability of resin-based luting cements. Dent Mater J 2010; 29: 316-23. [CrossRef]
- 36. Wegner SM, Kern M. Long-term resin bond strength to zirconia ceramic. J Adhes Dent 2000; 2: 139-47.
| APA | TUNCEL İ, TURP I (2018). Effects of coloring procedures on shear bond strength between resin cement and colored zirconia. , 122 - 126. 10.26650/eor.2018.440 |
| Chicago | TUNCEL İlkin,TURP Isil Effects of coloring procedures on shear bond strength between resin cement and colored zirconia. (2018): 122 - 126. 10.26650/eor.2018.440 |
| MLA | TUNCEL İlkin,TURP Isil Effects of coloring procedures on shear bond strength between resin cement and colored zirconia. , 2018, ss.122 - 126. 10.26650/eor.2018.440 |
| AMA | TUNCEL İ,TURP I Effects of coloring procedures on shear bond strength between resin cement and colored zirconia. . 2018; 122 - 126. 10.26650/eor.2018.440 |
| Vancouver | TUNCEL İ,TURP I Effects of coloring procedures on shear bond strength between resin cement and colored zirconia. . 2018; 122 - 126. 10.26650/eor.2018.440 |
| IEEE | TUNCEL İ,TURP I "Effects of coloring procedures on shear bond strength between resin cement and colored zirconia." , ss.122 - 126, 2018. 10.26650/eor.2018.440 |
| ISNAD | TUNCEL, İlkin - TURP, Isil. "Effects of coloring procedures on shear bond strength between resin cement and colored zirconia". (2018), 122-126. https://doi.org/10.26650/eor.2018.440 |
| APA | TUNCEL İ, TURP I (2018). Effects of coloring procedures on shear bond strength between resin cement and colored zirconia. European oral research (Online), 52(3), 122 - 126. 10.26650/eor.2018.440 |
| Chicago | TUNCEL İlkin,TURP Isil Effects of coloring procedures on shear bond strength between resin cement and colored zirconia. European oral research (Online) 52, no.3 (2018): 122 - 126. 10.26650/eor.2018.440 |
| MLA | TUNCEL İlkin,TURP Isil Effects of coloring procedures on shear bond strength between resin cement and colored zirconia. European oral research (Online), vol.52, no.3, 2018, ss.122 - 126. 10.26650/eor.2018.440 |
| AMA | TUNCEL İ,TURP I Effects of coloring procedures on shear bond strength between resin cement and colored zirconia. European oral research (Online). 2018; 52(3): 122 - 126. 10.26650/eor.2018.440 |
| Vancouver | TUNCEL İ,TURP I Effects of coloring procedures on shear bond strength between resin cement and colored zirconia. European oral research (Online). 2018; 52(3): 122 - 126. 10.26650/eor.2018.440 |
| IEEE | TUNCEL İ,TURP I "Effects of coloring procedures on shear bond strength between resin cement and colored zirconia." European oral research (Online), 52, ss.122 - 126, 2018. 10.26650/eor.2018.440 |
| ISNAD | TUNCEL, İlkin - TURP, Isil. "Effects of coloring procedures on shear bond strength between resin cement and colored zirconia". European oral research (Online) 52/3 (2018), 122-126. https://doi.org/10.26650/eor.2018.440 |